Description
- Two-part silicone elastomer dispersed in xylene
- Cures to a smooth silicone film that decreases the coefficient of friction (CoF) compared to the uncoated silicone and increases abrasion resistance for moving, sliding, and rubbing parts
- Provides adhesion to silicone substrates that results in a reduction of surface tack
- 1:1 Mix Ratio (Part A: Part B)
Applications
- To provide a heat-cured, low-friction coating on cured silicone substrates
- Apply by spraying for best results (dipping may also be utilized)
Product Details
| Property | Average Result |
|---|---|
| Viscosity | 24 cP (24 mPa*s) |
| Non Volatile Content | 25 % |
| Appearance | Translucent |
| Cure | 5 minutes / RTV |
| Cure System | Platinum |
| Mix Ratio | 1:1 |
| Post Cure | 5 minutes / 150 °C |
| Specific Gravity | 0.96 |
| Work Time | 24 hours |
| Comment | Requires minimum heat to cure. Acetic acid cure by-product therefore not recommended where corrosion is of concern. |